High temperature binder

The high-temperature adhesive is specially designed and formulated for the bonding between fiber products or for the fast pasting of the veneer on the kiln wall.It is composed of two components of liquid and powder, and it can be mixed into a slurry when feeding, or it can be divided and mixed and used on site.

Product Features:

High temperature resistance, matching with the temperature resistance of the fiber, bonding strength glue, no damage to the fiber after sintering, small drying and baking shrinkage

Special Note:

1. The part to be pasted must be dry, clean, free of scum, oil, and glaze.

2. Stir it evenly when using it. If it is too thick, add some clear water to adjust it.

performance:
1. Appearance: brown (or yellow-white) viscous liquid.
2. Content: ≥90%
3. Temperature resistance: 1750℃, 1800℃ or higher in a short time.
4. Surface drying: 0.5 hours
5. Minimum recoating interval: 2 hours
6. Hardness: 5H
7. Good oil resistance; acid and alkali resistance.
8. Coating thickness: According to the customer's own needs, it can be any thickness, but it must be sprayed or brushed layer by layer during the construction process. If a thicker thickness is required, the first layer can be applied first, and the thickness can be controlled at 1 -5mm, and then completely dry at a low temperature of about 70 ℃ or at room temperature before continuing to apply the second layer, followed by the third layer, and the fourth layer.Only after it is completely dried can it be used tightly at high temperature.

unique advantage

1. Good high-temperature performance: When using this product to repair various industrial kilns, there is no need to stop the furnace to cool down, and it can be directly sprayed and repaired and put into operation.Greatly shorten the repair time of the furnace lining, reduce the production cost, improve the work efficiency, and the energy saving effect is obvious;

2. High mechanical strength: Under the action of high temperature of 1000 degrees, this product has high bonding strength with refractory materials, abrasion resistance, shock resistance, peeling resistance, firmness and durability, and the refractoriness can reach 1750 degrees.

3. Convenient on-site construction: construction is not affected by seasonal climate and temperature, and is quick and convenient;

4. Longer service life: using this product, its service life is 7-10 times that of the transmission refractory materials currently used in China

Product index

Refractoriness\"℃1550

Bulk density 3.22g/c㎡

Load softening temperature\"1420℃

Thermal shock stability times≥20≥20 (850℃, water cooling)

Drying apparent porosity is 19% (110℃×24h)

Compressive strength after firing MPa 46.5 (500℃×2h) 52.3 (1000℃×2h) 89.1 (1400℃×2h)

Bonding time 45 seconds

Bond strength after firing MPa 5.84(900℃×3h) 5..67(1100℃×3h)

Main application range:
It is widely used in ceramics and metal products.The paint is a water-based paint, which is dried and formed at room temperature when used, and the hardness can reach more than 5H after drying and forming.The surface of the substrate should be clean and dry, free of grease, dust, salt and other impurities. The damaged area should be manually cleaned and repaired. When using, it can be coated with a thickness of 0.1mm to several centimeters according to specific requirements. If the spray is too sticky Thickness can be diluted by adding 5%-10% deionized water, and then sprayed. After the paint film is formed, it can protect the surface of ceramic, glass, metal and other coating materials from oxidation, and can also isolate the high temperature from the Damage caused by coating equipment.At the same time, the coating material can change the performance of the coating by adding functional materials. If 1%-3% of inorganic photocatalytic nano titanium dioxide powder is added to the inorganic coating material, it can be used as a photocatalytic coating; if added to the coating Ultra-fine molybdenum disulfide, etc., can improve the scratch resistance and hardness of the coating; if black inorganic copper oxide, iron black, manganese and other powders are added, the color of the coating can be changed, so that the coating can be used on the bottom of the pot. Local trial work for substantia nigra materials.The above added functional materials must be thoroughly mixed with the paint before use.